| PHYSICAL PROPERTIES | Value | Unit | Standard |
|---|---|---|---|
| Density | 1.29 | g/cm³ | ISO 1183 |
| Water absorption (24 h) | 0.3 | % | ISO 62 |
| Moisture absorption (23 °C / 50 % r.h.) | 0.4 | % | ISO 62 |
| Warpage (plate 91×91×2 mm) | 0.3 / 0.3 | mm | internal |
| Vicat softening (VST/B/50) | 70 | °C | ISO 306 |
| MECHANICAL PROPERTIES | Value | Unit | Standard |
|---|---|---|---|
| Tensile impact strength (+23 °C) | 3.5 | kJ/m² | ISO 8256 |
| Charpy impact strength (+23 °C) | 5.3 | kJ/m² | ISO 179-1/eU |
| Charpy notched (−23 °C) | NB | kJ/m² | ISO 179-1/eU |
| Tensile modulus | 1900 | MPa | ISO 527 |
| Elongation at break | 37 | % | ISO 527 |
| Flexural strength | 54.8 | MPa | ISO 178 |
| Flexural modulus | 2100 | MPa | ISO 178 |
| THERMAL PROPERTIES | Value | Unit | Standard |
|---|---|---|---|
| Vicat softening temp. (VST/B/50) | 70 | °C | ISO 306 |
| HDT (1.80 MPa) | 64 | °C | ISO 75 |
| HDT (0.45 MPa) | 73 | °C | ISO 75 |
| Coefficient of thermal expansion | 6.0×10⁻⁵ | 1/K | ISO 11359 |
| FIRE BEHAVIOUR | Value | Unit | Standard |
|---|---|---|---|
| Flammability (3.0 mm) | HB | — | UL94 |
| Flammability (1.5 mm) | HB | — | UL94 |
| FLOW BEHAVIOUR | Value | Unit | Standard |
|---|---|---|---|
| Spiral flow (1.5 mm, 260 °C) | 6.1 / 21 | cm | Tm = 260 °C |